product
name
|
main
component
|
viscosity
cps/25℃
|
Solid content
|
PH value
|
Functionality
|
Product characteristics
|
Main purpose
|
|
RUW-3087B
|
Waterborne polyurethane acrylate
|
≤450
|
40±2%
|
7-9
|
three
|
Fast curing speed, excellent toughness, excellent wear resistance, good powder dispersion effect, excellent adhesion and water resistance on plastic substrates, and good storage stability.
|
Recommended for UV matte keyboard coatings.
|
|
RUW-8083B
|
Waterborne polyurethane acrylate
|
≤450
|
thirty-eight±2%
|
7-9
|
eight
|
Fast curing speed, high hardness, excellent wear resistance, good powder dispersion effect, good leveling performance, excellent adhesion and water resistance on plastic substrates, and good storage stability.
|
Recommended for UV matte keyboard coatings.
|
|
RUW-8096B
|
Waterborne polyurethane acrylate
|
200-800
|
50±2%
|
7-9
|
eight
|
High solid content, high functionality, and good storage stability; It has fast curing speed, high hardness, excellent wear resistance, good powder dispersion effect, and no cracking; Excellent adhesion and water resistance on plastic substrates, boiled at 85 ℃ for 0.5 hours, without peeling off, no appearance change, and excellent storage stability.
|
Recommended for UV matte keyboard coatings.
|
|
RUW-8113B
|
Waterborne polyurethane acrylate
|
100-800
|
50±2%
|
7-9
|
eight
|
High solid content and high functionality; It has fast curing speed, high hardness, excellent wear resistance, resistance to wool felt, good dispersion effect of matte powder, and no cracking; Excellent adhesion and water resistance on plastic substrates, boiled at 85 ℃ for 0.5 hours, without peeling off, no appearance change, and excellent storage stability.
|
Recommended for UV matte keyboard coating with sheepskin felt.
|
|
RUW-1082B
|
Waterborne polyurethane acrylate
|
200-800
|
50±2%
|
7-9
|
ten
|
High solid content, high functionality, and good storage stability; It has fast curing speed, high hardness, excellent wear resistance, good powder dispersion effect, and no cracking; Excellent adhesion and water resistance on plastic substrates. Boiled at 85 ℃ for 2 hours, no peeling of the cells, no change in appearance, and excellent storage stability.
|
Recommended for UV matte coatings.
|
|
RUW-1022B
|
Waterborne polyurethane acrylate
|
200-1000
|
50±2%
|
7-9
|
ten
|
High solid content, high functionality, and good storage stability; It has fast curing speed, high hardness, excellent wear resistance, good powder dispersion effect, and no cracking; Excellent adhesion and water resistance on plastic substrates, boiled at 85 ℃ for 0.5 hours, without peeling off, no appearance change, and excellent storage stability.
|
Recommended for UV matte coatings.
|
|
RUW-1002B
|
Waterborne polyurethane acrylate
|
＜500
|
forty-six±2%
|
6.5-8.5
|
ten
|
Excellent directional silver powder with low glossiness; Excellent wear resistance, RCA>250 times in silver powder paint, can be recoated after 72 hours; Good adhesion on substrates such as PC and ABS PC; Excellent water resistance, boiled at 85 ℃ for half an hour, with no peeling off of the 100 grids and no change in appearance; Good storage stability.
|
Recommended for one coat of silver powder paint.
|
|
RUW-1116A
|
Waterborne polyurethane acrylate
|
100-800
|
forty-six±2%
|
7-9
|
ten
|
Excellent directional silver powder with low glossiness; Excellent wear resistance, RCA>250 times in silver powder paint, can be recoated after 72 hours; Good adhesion on substrates such as PC and ABS PC; Excellent water resistance, boiled at 85 ℃ for half an hour, with no peeling off of the 100 grids and no change in appearance; Good storage stability.
|
Recommended for one coat of silver powder paint.
|
|
RUW-8104B
|
Waterborne polyurethane acrylate
|
＜500
|
38±2%
|
7-9
|
eight
|
Excellent directional silver powder with low glossiness; Excellent wear resistance, can be recoated within 48 hours; Good adhesion on substrates such as PC and ABS PC; Excellent water resistance, boiled at 85 ℃ for half an hour, without any residue
Falling off, no change in appearance; Good storage stability.
|
Recommended for one coat of silver powder paint.
|
|
RUW-8105B
|
Waterborne polyurethane acrylate
|
＜500
|
thirty-eight±2%
|
7-9
|
eight
|
Excellent directional silver powder with low glossiness; Can be repainted within 48 hours; Good adhesion on substrates such as PC and ABS PC; Excellent water resistance, boiled at 85 ℃ for half an hour, with no peeling off of the 100 grids and no change in appearance; Good storage stability.
|
Recommended for one coat of silver powder paint
|
|
RUW-8202B
|
Waterborne polyurethane acrylate
|
＜500
|
thirty-eight±2%
|
7-9
|
eight
|
Excellent directional silver powder with low glossiness; Excellent wear resistance, can be recoated within 48 hours; Good adhesion on substrates such as PC and ABS PC; Excellent water resistance, boiled at 85 ℃ for half an hour, with no peeling off of the 100 grids and no change in appearance; Good storage stability.
|
Recommended for one coat of silver powder paint.
|
|
RUW-1085A
|
Waterborne polyurethane acrylate
|
200-1000
|
52±2%
|
6.5-8.5
|
ten
|
Excellent fingerprint and oil resistant pen performance, high solid content, high functionality, and good storage stability; It has fast curing speed, high hardness, excellent wear resistance, good powder dispersion effect, and no cracking; Excellent adhesion and water resistance on plastic substrates, boiled at 85 ℃ for 0.5 hours.
|
Recommended for UV matte anti fouling coatings.
|
|
RUW-1087A
|
Waterborne polyurethane acrylate
|
≤500
|
four0±2%
|
6.5-8.5
|
ten
|
Excellent fingerprint and oil resistant pen performance, high solid content, high functionality, and good storage stability; It has fast curing speed, high hardness, excellent wear resistance, good powder dispersion effect, and no cracking; Excellent adhesion and water resistance on plastic substrates, boiled at 85 ℃ for 0.5 hours.
|
Recommended for UV matte anti fouling coatings.
|
|
RUW-1088A
|
Waterborne polyurethane acrylate
|
100-800
|
five0±2%
|
7-9
|
ten
|
Has excellent fingerprint resistance and oil pen performance. High solid content, high functionality, and good storage stability; It has fast curing speed, high hardness, excellent wear resistance, good powder dispersion effect, and no cracking; Excellent adhesion and water resistance on plastic substrates, boiled at 85 ℃ for 0.5 hours.
|
Recommended for UV matte anti fouling coatings.
|
|
RUW-1088H
|
Waterborne polyurethane acrylate
|
100-800
|
five0±2%
|
7-9
|
ten
|
Has excellent fingerprint resistance and oil pen performance. High solid content, high functionality, and good storage stability; It has fast curing speed, high hardness, excellent wear resistance, good powder dispersion effect, and no cracking; Excellent adhesion and water resistance on plastic substrates, boiled at 85 ℃ for 0.5 hours.
|
Recommended for UV matte anti fouling coatings.
|
|
RUW-8190H
|
Waterborne polyurethane acrylate
|
10-100
|
forty-two±2%
|
6.5-8.5
|
eight
|
Excellent fingerprint and oil resistant pen performance. High functionality and good storage stability; It has fast curing speed, high hardness, excellent wear resistance, good powder dispersion effect, and no cracking; On a plastic base
Excellent adhesion and water resistance on the material, boiled at 85 ℃ for 0.5 hours.
|
Recommended for UV matte anti fouling coatings.
|
|
RUW-8184B
|
Waterborne polyurethane acrylate
|
≤500
|
four0±2%
|
7-9
|
eight
|
Excellent fingerprint and oil resistant pen performance. High solid content, high functionality, and good storage stability; It has fast curing speed, high hardness, excellent wear resistance, good powder dispersion effect, and no cracking;
Excellent adhesion and water resistance on plastic substrates, boiled at 85 ℃ for 2 hours.
|
Recommended for UV matte anti fouling coatings.
|
|
RUW-8186B
|
Waterborne polyurethane acrylate
|
100-800
|
four0±2%
|
7-9
|
eight
|
Strong hand feel, good stain resistance, good self extinction, good scratch repair resistance, wear and chemical resistance, etc; High functionality and good storage stability; Its curing speed is fast, its hardness is high, and it is resistant to
Excellent grinding without cracking; Excellent adhesion and water resistance on plastic substrates, boiled at 85 ℃ for 30 minutes.
|
Recommended for UV matte hand anti fouling coatings.
|
|
RUW-8206B
|
Waterborne polyurethane acrylate
|
600-1600
|
thirty-seven±2%
|
7-9
|
eight
|
Strong hand feel, good stain resistance, good self extinction, good scratch repair resistance, wear and chemical resistance, etc; High functionality and good storage stability; Its curing speed is fast, its hardness is high, and it is resistant to
Excellent grinding without cracking; Excellent adhesion and water resistance on plastic substrates, boiled at 85 ℃ for 30 minutes.
|
Recommended for UV matte hand anti fouling coatings.
|
|
RUW-8004B
|
Waterborne polyurethane acrylate
|
100-600
|
47±2%
|
7-9
|
eight
|
High functionality, superior workability, and fast curing speed; Soft and delicate feel; Good scratch resistance, wear resistance, and RCA resistance; Good adhesion on substrates such as PC, ABS, and ABS PC; Good water boiling resistance and storage stability.
|
Recommended for UV tactile coatings.
|
|
RUW-8120B
|
Waterborne polyurethane acrylate
|
100-800
|
37±2%
|
7-9
|
eight
|
Strong hand feel, good self extinction, good scratch repair resistance, wear and chemical resistance, etc; High functionality and good storage stability; It has fast curing speed, high hardness, excellent wear resistance, and no cracking; Excellent adhesion and water resistance on plastic substrates, boiled at 85 ℃ for 30 minutes.
|
Recommended for UV tactile coatings.
|
|
RUW-8124B
|
Waterborne polyurethane acrylate
|
100-800
|
thirty-seven±2%
|
7-9
|
eight
|
Strong hand feel, good stain resistance, good self extinction, good scratch repair resistance, wear and chemical resistance, etc; High functionality and good storage stability; Its curing speed is fast, its hardness is high, and it is resistant to
Excellent grinding without cracking; Excellent adhesion and water resistance on plastic substrates, boiled at 85 ℃ for 30 minutes.
|
Recommended for UV matte hand anti fouling coatings.
|
|
RUW-3302B
|
Waterborne polyurethane acrylate
|
100-1000
|
fifty-six±2%
|
4-6
|
three
|
Has excellent luster and high gloss, high fullness, high hardness, and other characteristics; Excellent water and chemical resistance, with good adhesion on plastic substrates. Boiled at 85 ℃ for 30 minutes.
|
Recommended for high gloss coatings such as plastic paint and metal paint.
|
|
RUW-2025B
|
Waterborne polyurethane acrylate
|
100-800
|
fifty-two±2%
|
7-9
|
two
|
Good adhesion and flexibility on substrates such as PC and ABS PC, with no cracking when folded in half; Improved yellowing resistance; Boil in water at 85 ℃ for half an hour, without shedding, with good storage stability.
|
Recommended for coatings that require flexibility.
|
|
RUW-6018B
|
Waterborne polyurethane acrylate
|
200-800
|
fifty±2%
|
7-9
|
six
|
High functionality and good storage stability; It has fast curing speed, high hardness, excellent wear resistance, good fullness, and is easy to construct; Excellent adhesion and water resistance on plastic substrates, boiled at 85 ℃ for 0.5 hours, without peeling off, no appearance change, and excellent storage stability.
|
Recommended for water-based UV high gloss coatings.
|
|
RUW-6030B
|
Waterborne polyurethane acrylate
|
100-900
|
fifty-five±2%
|
7-9
|
six
|
High functionality and good storage stability; It has fast curing speed, high hardness, excellent wear resistance, good fullness, and is easy to construct; Excellent adhesion and water resistance on plastic substrates, boiled at 85 ℃ for 0.5 hours, without peeling off, no appearance change, and excellent storage stability.
|
Recommended for water-based UV high gloss coatings.
|
|
RUW-3002B
|
Waterborne polyurethane acrylate
|
≤500
|
forty-two±2%
|
7-9
|
three
|
Anionic water-based adhesion promoting resin can significantly improve adhesion and water boiling resistance with plastic substrates such as PC, ABS, and ABS PC; Excellent stability and long-term effectiveness, excellent dispersibility and wettability.
|
Recommended for plastic substrates that require improved adhesion and boiling.
|
|
RUW-4002B
|
Waterborne polyurethane acrylate
|
≤500
|
forty-seven±2%
|
7-9
|
four
|
High leveling, fast curing speed, good adhesion and water resistance on plastic substrates such as PC, ABS, ABS, and PC; Excellent stability and long-term effectiveness, excellent dispersibility and wettability.
|
Recommended for plastic substrates that require improved leveling and adhesion.
|
|
RUW-6002B
|
Waterborne polyurethane acrylate
|
≤500
|
forty-nine±2%
|
7-9
|
six
|
High hardness, high wear resistance, fast curing speed, good adhesion and water resistance on plastic substrates such as PC, ABS, ABS, and PC; Excellent stability and long-term effectiveness, excellent dispersibility and wettability.
|
Recommended for plastic substrates that require increased hardness and wear resistance.
|
|
RAW2140
|
Aqueous hydroxyacrylic acid lotion
|
≤200
|
forty±2%
|
8-10
|
Hydroxyl value 1.0%
|
Small particle size, transparent appearance；Fast drying speed and good initial adhesion resistance；Excellent transparency of dry and wet film；High extinction efficiency and good scratch resistance；Good adhesion of substrate。
|
Recommended for primer, topcoat, and solid color topcoat
|
|
RAW2240
|
Aqueous hydroxyacrylic acid lotion
|
300-500
|
forty-two±2%
|
6.5-8.5
|
Hydroxyl value 1.9%
|
Excellent gloss and fullness；Fast drying speed and good initial adhesion resistance；Fast hardness establishment speed；Good adhesion to metal and plastic substrates。
|
Recommended for silver primer, solid primer, and clear topcoat
|
|
RAW2340
|
Waterborne acrylic lotion
|
10-20
|
forty±2%
|
8-10
|
MFFT45℃
|
Lotion has transparent appearance and good dry film transparency；Fast drying speed and high final hardness；Excellent water and chemical resistance；Good adhesion of PC, ABS, and ABS PC substrates；Good wetting performance of the substrate。
|
Recommended for clear primer, solid primer
|
|
RAW9240
|
Waterborne acrylic lotion
|
＜200
|
forty±2%
|
8-10
|
MFFT15℃
|
Good flexibility of paint film；Good adhesion to substrates such as ABS and PC
Good color paste compatibility；Good compatibility with conventional lotion；Faster increase in adhesion at room temperature；Good adhesion with UV layers。
|
Recommended for plastic toy paint and plastic adhesion primer
|